PE Pipe grade polyethylene compound
PE Pipe grade polyethylene compound
Pipe grade polyethylene compound according to the standard for the production of drinking water pipes according to the standard and COA
PE Pipe grade polyethylene compound
Pipe grade polyethylene compound
Pipe grade polyethylene compound according to the standard for the production of drinking water pipes according to the standard and COA
کامپاند پلی اتیلن گرید لوله مطابق با استاندارد جهت تولید لولههای آب آشامیدنی مطابق استاندارد و جدول آنالیز محصول
PROPERTY
MELT FLOW INDEX (190 °C, 2.16 Kg)
Density(method A-metanol 23-C)
Carbon Blak Content
Ash content
Disp/Carbon Black
UNIT ISO-1133A,isiri6980-1
TYPICAL VALUE
ISO1-1183.isiri7090-1,2
0.22gr/10min 0.953gr/Cm?
Pipe grade polyethylene compound
ASTM D1693
2.21
2%750 ≥20 Mpa ≥25 Mpa
≥ 40 min.
140°C
> 1000 hr
179mg/kg
0.02
14
Pipe grade polyethylene compound
Elongation at Break
[Yield Strength]
Tensil Strength at Break
Oxidation Induction Time 210-C Melting Point
Escr (50 C, A:%10 Igepal Co-630)
Total Volatiles
EN 12099
ASTM D1693
2.21
2%750 ≥20 Mpa ≥25 Mpa
≥ 40 min.
140°C
> 1000 hr
179mg/kg
0.02
14
Pipe grade polyethylene compound
Elongation at Break
[Yield Strength]
Tensil Strength at Break
Oxidation Induction Time 210-C Melting Point
Escr (50 C, A:%10 Igepal Co-630)
Total Volatiles
EN 12099
PROPERTY
MELT FLOW INDEX (190 °C, 2.16 Kg)
Density(method A-metanol 23-C)
Carbon Blak Content
Ash content
Disp/Carbon Black
UNIT ISO-1133A,isiri6980-1
TYPICAL VALUE
ISO1-1183.isiri7090-1,2
0.22gr/10min 0.953gr/Cm?